Autolad1G
特点
● 适用于无铅制程，并具有优异的耐离子迁移性能
● 在超薄规格上兼备较低Z轴CTE及优异尺寸稳定性
● 不含卤素、锑、红磷等成分
应用领域
适用于HDI汽车电子，如摄像头模组等
- 产品性能
- 产品证书
- 资料下载
| Items | Method | Condition | Unit | Typical Value | |
| Tg | IPC-TM-650 2.4.25D | DSC | ℃ | 173 | |
| Td | IPC-TM-650 2.4.24.6 | TGA(5% W.L) | ℃ | 400 | |
| T288 | IPC-TM-650 2.4.24.1 | TMA | min | 60 | |
| CTE (Z-axis) | IPC-TM-650 2.4.24 | Before Tg | ppm/℃ | 35 | |
| After Tg | ppm/℃ | 189 | |||
| 50-260℃ | % | 2.3 | |||
| DK (RC:50%) | 1GHz | IPC-TM-650 2.5.5.9 | C-24/23/50 | -- | 4.30 |
| 10GHz | IPC-TM-650 2.5.5.5 | -- | 4.05 | ||
| Df (RC:50%) | 1GHz | IPC-TM-650 2.5.5.9 | C-24/23/50 | -- | 0.010 |
| 10GHz | IPC-TM-650 2.5.5.5 | -- | 0.012 | ||
| Volume Resistivity | IPC-TM-650 2.5.17.1 | C-96/35/90 | MΩ.cm | 6.00E+08 | |
| Surface Resistivity | IPC-TM-650 2.5.17.1 | C-96/35/90 | MΩ | 8.00E+07 | |
| Dielectric Breakdown | IPC-TM-650 2.5.6 | D-48/50+D-0.5/23 | kV | 45+Kv NB | |
| Peel Strength (1 oz) | IPC-TM-650 2.4.8 | 288℃,10s | N/mm[lb/in] | 1.35 [7.71] | |
| Flexural Strength (LW/CW) | IPC-TM-650 2.4.4 | A | MPa | 550/430 | |
| Flexural Modulus (LW/CW) | IPC-TM-650 2.4.4 | A | GPa | 28/25 | |
| Water Absorption | IPC-TM-650 2.6.2.1 | D-24/23 | % | 0.09 | |
| Flammability | UL94 | C-48/23/50 | Rating | V-0 | |
Remarks:
Remark:
1. All the typical value is based onthe 1.6mm (8*7628) specimen. The Dk and Df value based on 50% RC.
2. All the typical value listed above isfor your reference only, please turn to Shengyi Technology Co., Ltd for detailedinformation, and all rights from this data sheet are reserved by ShengyiTechnology Co., Ltd.
Explanations:C=Humidity conditioning; D=Immersion conditioning in distilled water;E=Temperature conditioning.
The figures following the letter symbolsindicate with the first digit the duration of the preconditioning in hours,with the second digit the preconditioning temperature in ℃ and with the third digit the relative humidity.